- 熔體流動(dòng)速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.923
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in3 | ExxonMobil Method | ||
| Thickness | 25.4 microns | 1.00 mil | |||
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.3 MPa | 1500 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 | ||
| Film Elongation at Break, TD | 590 % | 590 % | ASTM D882 | ||
| Puncture Energy | 1.76 J | 1.30 ft-lb | Exxon Mobil Method | ||
| Elmendorf Tear Strength, MD | 9.45 g/micron | 240 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 18.9 g/micron | 480 g/mil | ASTM D1922 | ||
| Dart Drop | 6.69 g/micron | 170 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 43.4 MPa | 6300 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 32.4 MPa | 4700 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 231 MPa | 33500 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 241 MPa | 34900 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 122 °C | 252 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 25 % | 25 % | ASTM D1003 | ||
| Gloss | 25 % | 25 % | 45°, MD; ASTM D2457 | ||
| 27 % | 27 % | 45°, TD; ASTM D2457 | |||
| Descriptive Properties | |||||
| Features | PPA and Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.