- 熔體流動速率 [g/10min]: 2.25
- 密度 [g/cm3]: 0.921
- 拉伸強度 [MPa]: 11.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | ExxonMobil Method | ||
| Melt Flow | 2.25 g/10 min | 2.25 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 90 | 90 | 15s; ASTM D2240 | ||
| Hardness, Shore D | 44 | 44 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 | ||
| Tensile Strength, Yield | 11.6 MPa | 1680 psi | ASTM D638 | ||
| Elongation at Break | 625 % | 625 % | ASTM D638 | ||
| Elongation at Yield | 14 % | 14 % | ASTM D638 | ||
| 1% Secant Modulus | 243 MPa | 35200 psi | ASTM D790 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 7.61e+15 ohm-cm | 7.61e+15 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 2.17 @Frequency 60 Hz | 2.17 @Frequency 60 Hz | ASTM D150 | ||
| Dielectric Strength | 49.6 kV/mm | 1260 kV/in | ASTM D149 | ||
| Dissipation Factor | 0.000010 @Frequency 60 Hz | 0.000010 @Frequency 60 Hz | ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 109 °C | 228 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 93.9 °C | 201 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.