- 熔體流動速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.912
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.912 g/cc | 0.0329 lb/in3 | ASTM D1505 | ||
| Thickness | 20.3 microns | 0.800 mil | |||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 7.52 MPa | 1090 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 5.72 MPa | 830 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 410 % | 410 % | ASTM D882 | ||
| Film Elongation at Break, TD | 735 % | 735 % | ASTM D882 | ||
| Puncture Energy | 4.64 J | 3.42 ft-lb | Exxon Mobil Method | ||
| Elmendorf Tear Strength MD | 120 g | 120 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 520 g | 520 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 5.91 g/micron | 150 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 25.6 g/micron | 650 g/mil | ASTM D1922 | ||
| Dart Drop | 8.366 g/micron | 212.5 g/mil | ASTM D1709 | ||
| Dart drop Test | 170 g | 0.375 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 76.60 MPa | 11110 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 49.2 MPa | 7140 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 80.53 MPa | 11680 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 105.6 MPa | 15320 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 113 °C | 235 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 99.0 °C | 210 °F | ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.6 % | 1.6 % | ASTM D1003 | ||
| Gloss | 90 % | 90 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||