- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.923
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in3 | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 100 % | 100 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Secant Modulus, MD | 0.240 GPa | 34.8 ksi | ASTM D882 |
| Secant Modulus, TD | 0.280 GPa | 40.6 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 500 g | 500 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 100 g | 100 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 15.7 g/micron | 400 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 |
| Dart Drop | 1.89 g/micron | 48.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 60.0 g | 0.132 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 33.0 MPa | 4790 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 112 °C | 234 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 65 % | 65 % | 45°, ASTM D-2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |