- 熔體流動速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 2.3 g/10 min | 2.3 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.70 MPa | 1410 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Secant Modulus, MD | 0.190 GPa | 27.6 ksi | ASTM D882 |
| Secant Modulus, TD | 0.210 GPa | 30.5 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 300 g | 300 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 9.45 g/micron | 240 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 6.30 g/micron | 160 g/mil | ASTM D1922 |
| Dart Drop | 2.05 g/micron | 52.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 65.0 g | 0.143 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 28.0 MPa | 4060 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 109 °C | 228 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % | 8.0 % | ASTM D1003 |
| Gloss | 55 % | 55 % | 45°, ASTM D-2457 |