- 熔體流動速率 [g/10min]: 26.0
- 密度 [g/cm3]: 0.919
- 拉伸強度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ExxonMobil Method |
| Melt Flow | 26 g/10 min | 26 g/10 min | 190oC/2.16 kg; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 86 | 86 | 15s; ASTM D2240 |
| Hardness, Shore D | 42 | 42 | 15s; ASTM D2240 |
| Tensile Strength at Break | 7.58 MPa | 1100 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| 1% Secant Modulus | 234 MPa | 34000 psi | ASTM D790 |
| Impact Test | 16.3 J | 12.0 ft-lb | @ 73oF, Instrumented Impact Total Energy; ASTM D3763 |
| 19.0 J | 14.0 ft-lb | @ -4oF, Instrumented Impact Total Energy at -20°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 83.9 °C | 183 °F | ASTM D1525 |