- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.918
- 彎曲強度 [MPa]: 9.6
- 彎曲模量 [MPa]: 0.186
- 脆化溫度 [℃]: -72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | <= 1.0 hour | <= 1.0 hour | F50, Condition A; ASTM D-1693 |
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength, Ultimate | 9.60 MPa | 1390 psi | ASTM D638 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Flexural Modulus | 0.186 GPa | 27.0 ksi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.25 @Frequency 1e+6 Hz | 2.25 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 20.4 kV/mm @Thickness 3.17 mm | 518 kV/in @Thickness 0.125 in | ASTM D149 |
| Dissipation Factor | 0.00010 @Frequency 1e+6 Hz | 0.00010 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 108 °C | 226 °F | Exxon Method |
| Brittleness Temperature | <= -72.0 °C | <= -97.6 °F | ASTM D746 |