- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.917
- 彎曲強度 [MPa]: 9.0
- 彎曲模量 [MPa]: 0.165
- 脆化溫度 [℃]: -67.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | <= 5.0 hour | <= 5.0 hour | F50, Condition A; ASTM D-1693 |
| Melt Flow | 12 g/10 min | 12 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48 | 48 | ASTM D2240 |
| Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
| Elongation at Break | 760 % | 760 % | ASTM D638 |
| Flexural Modulus | 0.165 GPa | 23.9 ksi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.03 @Frequency 1e+6 Hz | 2.03 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 14.2 kV/mm @Thickness 3.17 mm | 361 kV/in @Thickness 0.125 in | ASTM D149 |
| Dissipation Factor | 0.00010 @Frequency 1e+6 Hz | 0.00010 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 °C | 219 °F | Exxon Method |
| Brittleness Temperature | <= -67.0 °C | <= -88.6 °F | ASTM D746 |