- 密度 [g/cm3]: 1.62
- 缺口沖擊強度: 6.0
- 彎曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 125 MPa | 18100 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.5 % | 1.5 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | ISO 180/1A |
| Charpy Impact Unnotched | 3.00 J/cm2 | 14.3 ft-lb/in2 | ISO 179/1eU |
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 283 °C | 541 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-2 @Thickness 0.750 mm | V-2 @Thickness 0.0295 in | |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 95.0 - 120 °C | 203 - 248 °F | cavity |
| Melt Temperature | 295 - 310 °C | 563 - 590 °F | |
| Drying Temperature | >= 70.0 °C | >= 158 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | 0.030 % | 0.030 % | Necessary low maximum |