- 密度 [g/cm3]: 1.45
- 彎曲模量 [MPa]: 8.00
- 熱變形溫度 [℃]: 270.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ISO 1183 |
| Density of Compound | 1.42 g/cc | 0.0513 lb/in3 | melt; Internal |
| Viscosity Test | 85.0 cm3/g | 85.0 cm3/g | ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00800 cm/cm | 0.00800 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.00 % | 2.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 8.50 GPa | 1230 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm2 | 23.8 ft-lb/in2 | ISO 179/1eU |
| Charpy Impact, Notched | 0.800 J/cm2 | 3.81 ft-lb/in2 | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 560 V | 560 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 32.0 μm/m-°C | 17.8 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 85.0 μm/m-°C | 47.2 μin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.47 J/g-°C | 0.351 BTU/lb-°F | Internal |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft2-°F | Internal |
| Melting Point | 283 °C | 541 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Transformation Temperature, Tg | 105 °C | 221 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 270 °C | 518 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 262 °C | 504 °F | ISO 75-1, -2 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | UL94 |
| Oxygen Index | 29.0 % | 29.0 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature |
| 220 °C | 428 °F | Ejection temperature; Internal | |
| Melt Temperature | 300 °C | 572 °F | Optimum |
| 295 - 310 °C | 563 - 590 °F | ||
| 295 - 310 °C | 563 - 590 °F | ||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| 100 °C | 212 °F | Optimum | |
| Drying Temperature | >= 95.0 °C | >= 203 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |