- 熔體流動速率 [g/10min]: 30.0
- 密度 [g/cm3]: 1.38
- 缺口沖擊強度: 6.0
- 彎曲模量 [MPa]: 5.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in3 | ISO 1183 |
| Density of Compound | 1.14 g/cc | 0.0412 lb/in3 | melt; Internal |
| Viscosity Test | 85.0 cm3/g | 85.0 cm3/g | ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.00300 cm/cm | 0.00300 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00800 cm/cm | 0.00800 in/in | ISO 294-4 |
| Melt Flow | 30.0 g/10 min @Load 2.16 kg, Temperature 300 °C | 30.0 g/10 min @Load 4.76 lb, Temperature 572 °F | (MVR) cm3/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.30 % | 2.30 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 6.40 GPa | 928 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 155 MPa | 22500 psi | ISO 178 |
| Flexural Modulus | 5.80 GPa | 841 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | ISO 180/1A |
| Charpy Impact Unnotched | 3.50 J/cm2 | 16.7 ft-lb/in2 | ISO 179/1eU |
| 3.00 J/cm2 @Temperature -30.0 °C | 14.3 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO 179/1eA |
| 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 6000 MPa | 870000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 4600 MPa | 667000 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Strength | 41.0 kV/mm | 1040 kV/in | IEC 60243-1 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 μm/m-°C | 16.7 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C | 44.4 μin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.47 J/g-°C | 0.351 BTU/lb-°F | Internal |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft2-°F | Internal |
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Transformation Temperature, Tg | 105 °C | 221 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ISO 75-1, -2 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | UL94 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature |
| 230 °C | 446 °F | Ejection temperature; Internal | |
| Melt Temperature | 300 °C | 572 °F | Optimum |
| 295 - 310 °C | 563 - 590 °F | ||
| 295 - 310 °C | 563 - 590 °F | ||
| Mold Temperature | 100 °C | 212 °F | Optimum |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | >= 95.0 °C | >= 203 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |