- 密度 [g/cm3]: 1.2
- 缺口沖擊強度: 7.4
- 拉伸強度 [MPa]: 46.0
- 斷裂伸長率 [%]: 67.0
- 彎曲強度 [MPa]: 53.0
- 彎曲模量 [MPa]: 1.90
- 硬度: 105.0
- 熱變形溫度 [℃]: 73.0
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm | 0.0040 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 310 % | 310 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | ASTM D790 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
| Izod Impact, Notched | 7.40 J/cm | 13.9 ft-lb/in | ASTM D256 |
| 0.600 J/cm @Temperature -40.0 °C | 1.12 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.30 % | 0.30 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | Regular transmittance per ASTM D 1003 |
| 91 % | 91 % | Total Transmittance; ASTM D 1003 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 °C | 518 °F | |
| Mold Temperature | 22.5 °C | 72.5 °F | |
| Drying Temperature | 70.0 °C | 158 °F | |