- 密度 [g/cm3]: 1.2
- 缺口沖擊強度: 0.8
- 拉伸強度 [MPa]: 47.0
- 斷裂伸長率 [%]: 65.0
- 彎曲強度 [MPa]: 46.0
- 彎曲模量 [MPa]: 1.85
- 硬度: 103.0
- 熱變形溫度 [℃]: 73.0
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.20 mm | 0.0040 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | ISO 527 |
| 51.0 MPa | 7400 psi | ASTM D638 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | ASTM D638 and ISO 527 |
| Elongation at Break | 200 % | 200 % | ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527 |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | ISO 178 |
| 69.0 MPa | 10000 psi | ASTM D790 | |
| Flexural Modulus | 1.85 GPa | 268 ksi | ISO 178 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.400 J/cm @Temperature -40.0 °C | 0.749 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.30 % | 0.30 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | Regular transmittance per ASTM D 1003 |
| 91 % | 91 % | Total Transmittance; ASTM D 1003 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 255 °C | 491 °F | |
| Mold Temperature | 22.5 °C | 72.5 °F | |
| Drying Temperature | 70.0 °C | 158 °F | |