- 缺口沖擊強度: 0.75
- 拉伸強度 [MPa]: 45.0
- 彎曲模量 [MPa]: 1.80
- 硬度: 103.0
- 熱變形溫度 [℃]: 74.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Melt Density | 1.08 g/cc @Temperature 285 °C | 0.0390 lb/in3 @Temperature 545 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 340 % | 340 % | ASTM D638 |
| Flexural Strength | 66.0 MPa | 9570 psi | ASTM D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm @Temperature -40.0 °C | 1.41 ft-lb/in @Temperature -40.0 °F | ASTM D256 |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D4812 | |
| Puncture Energy | 42.0 J | 31.0 ft-lb | Puncture Resistance @Max Load, 23°C; ASTM D3763 |
| 52.0 J | 38.4 ft-lb | Puncture Resistance @Max Load, -40°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 75.0 μm/m-°C @Temperature 20.0 °C | 41.7 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.09 J/g-°C @Temperature 10.0 °C | 0.261 BTU/lb-°F @Temperature 50.0 °F | DSC |
| 1.14 J/g-°C @Temperature 30.0 °C | 0.272 BTU/lb-°F @Temperature 86.0 °F | DSC | |
| 1.64 J/g-°C @Temperature 100 °C | 0.392 BTU/lb-°F @Temperature 212 °F | DSC | |
| 1.86 J/g-°C @Temperature 180 °C | 0.445 BTU/lb-°F @Temperature 356 °F | DSC | |
| 2.16 J/g-°C @Temperature 290 °C | 0.516 BTU/lb-°F @Temperature 554 °F | DSC | |
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft2-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Vicat Softening Point | 86.0 °C | 187 °F | 1kg load; ASTM D1525 |
| Glass Transition Temp, Tg | 87.0 °C | 189 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |