- 密度 [g/cm3]: 1.23
- 拉伸強度 [MPa]: 46.0
- 熱變形溫度 [℃]: 78.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 4.4 % | 4.4 % | |
| Tensile Modulus | 2.09 GPa | 303 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.830 J/cm2 | 3.95 ft-lb/in2 | |
| 0.480 J/cm2 @Temperature -30.0 °C | 2.28 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 87.0 μm/m-°C @Temperature 20.0 °C | 48.3 μin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 70.0 μm/m-°C @Temperature 20.0 °C | 38.9 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 225 °C | 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |
| Vicat Softening Point | 83.0 °C | 181 °F | |
| Glass Transition Temp, Tg | 82.0 °C | 180 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 275 - 295 °C | 527 - 563 °F | |