- 密度 [g/cm3]: 1.63
- 吸水率 [%]: 0.9
- 彎曲模量 [MPa]: 10.0
- 熱變形溫度 [℃]: 270.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in3 | ISO 1183 |
| Water Absorption | 0.900 % | 0.900 % | ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00300 cm/cm | 0.00300 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00800 cm/cm | 0.00800 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 119 | 119 | ISO 2039-2 |
| Tensile Strength at Break | 114 MPa | 16500 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.50 % | 1.50 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.8 GPa | 1570 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 172 MPa | 24900 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.00 J/cm2 | 14.3 ft-lb/in2 | ISO 179/1eU |
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 440 V | 440 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 6.00 μm/m-°C | 3.33 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 μm/m-°C | 55.6 μin/in-°F | ISO 11359-2 |
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 270 °C | 518 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-2 @Thickness 0.800 mm | V-2 @Thickness 0.0315 in | UL94 |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL94 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature |
| Melt Temperature | 300 °C | 572 °F | Optimum |
| 295 - 310 °C | 563 - 590 °F | ||
| 295 - 310 °C | 563 - 590 °F | ||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| 100 °C | 212 °F | Optimum | |
| Drying Temperature | >= 95.0 °C | >= 203 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.0300 % | 0.0300 % | Necessary low maximum residual |
- 關(guān)鍵詞:
- PCT
- 供應(yīng)
- 30% Glass Reinforced
- Celanese THERMX CG933 PCT