- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 1.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 1.1 % | 1.1 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.9 % | 1.9 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 1mm/min; ISO 527-2/1A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 24.0 μm/m-°C | 13.3 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 75.0 μm/m-°C | 41.7 μin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.38 J/g-°C | 0.330 BTU/lb-°F | |