- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.6
- 缺口沖擊強度: 4.0
- 拉伸強度 [MPa]: 74.0
- 彎曲模量 [MPa]: 3.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ISO R 1183 | ||
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | DIN 53473 | ||
| Water Absorption at Saturation | 0.60 % @Temperature 20.0 °C | 0.60 % @Temperature 68.0 °F | ISO R 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 120 MPa | 17400 psi | Hc 30; ISO 2039; partially | ||
| Tensile Strength, Yield | 74.0 MPa | 10700 psi | ISO-DIS 527 | ||
| Creep Strength | 27.0 MPa | 3920 psi | 1% elongation, 1000 h; DIN 53444 | ||
| >= 45.0 MPa | >= 6530 psi | 2% elongation, 1000 h; DIN 53444 | |||
| Flexural Strength | 125 MPa | 18100 psi | DIN 54352 | ||
| Flexural Modulus | 3.50 GPa | 508 ksi | DIN 53457 | ||
| Compressive Strength | 56.0 MPa | 8120 psi | 5% pressing; EN ISO 604 | ||
| 88.0 MPa | 12800 psi | 10% pressing; EN ISO 604 | |||
| 95.0 MPa | 13800 psi | 20% pressing; EN ISO 604 | |||
| Izod Impact, Notched (ISO) | >= 4.00 kJ/m2 | >= 1.90 ft-lb/in2 | DIN 53453 | ||
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 | ||
| Coefficient of Friction | 0.020 - 0.080 | 0.020 - 0.080 | With lubrication | ||
| Coefficient of Friction, Dynamic | 0.24 - 0.28 | 0.24 - 0.28 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C | ||
| Tear Strength Test | >= 0.50 | >= 0.50 | ISO-DIS 527 | ||
| K Factor (Wear Factor) | 1.5e-10 | 1.5e-10 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | DIN 53482 | ||
| Surface Resistance | 5.00e+12 ohm | 5.00e+12 ohm | DIN 53482 | ||
| Dielectric Constant | 3.6 | 3.6 | DIN 53483 | ||
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | DIN 53481 | ||
| Dielectric Loss Index | 0.019 | 0.019 | DIN 53483 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 80.0 μm/m-°C @Temperature 20.0 - 100 °C | 44.4 μin/in-°F @Temperature 68.0 - 212 °F | DIN 53752 | ||
| Specific Heat Capacity | 1.05 J/g-°C | 0.251 BTU/lb-°F | |||
| Thermal Conductivity | 0.210 W/m-K | 1.46 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 255 °C | 491 °F | ISO R 1218 | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous | ||
| 180 °C | 356 °F | Intermittent | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | V-notch; ISO R 75 | ||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous | ||
| Descriptive Properties | |||||
| Creepage/leakage Resistance | Ka2 | DIN 53480 | |||