- 缺口沖擊強度: 1.18
- 拉伸強度 [MPa]: 40.2
- 彎曲模量 [MPa]: 1.87
- 硬度: 96.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0070 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 96 | 96 | ASTM D785 |
| Tensile Strength, Yield | 40.2 MPa | 5830 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 60.8 MPa | 8820 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.87 GPa | 272 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 6.35 mm | 2.20 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| 2.75 J/cm @Thickness 3.17 mm | 5.14 ft-lb/in @Thickness 0.125 in | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C @Thickness 6.40 mm | 176 °F @Thickness 0.252 in | ASTM D648 |
| Vicat Softening Point | 94.0 °C | 201 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm | HB @Thickness 0.0591 - 0.118 in | |
| Optical Properties | Metric | English | Comments |
| Yellow Index | 25 % @Thickness 3.20 mm | 25 % @Thickness 0.126 in | ASTM D1925 |