- 缺口沖擊強(qiáng)度: 1.96
- 拉伸強(qiáng)度 [MPa]: 41.2
- 彎曲模量 [MPa]: 1.72
- 硬度: 95.0
- 熱變形溫度 [℃]: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 26.5 MPa | 3840 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 41.2 MPa | 5970 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 17 % | 17 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.77 GPa | 256 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 49.0 MPa | 7110 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.72 GPa | 249 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 6.35 mm | 3.67 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| 4.41 J/cm @Thickness 3.17 mm | 8.27 ft-lb/in @Thickness 0.125 in | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 6.40 mm | 203 °F @Thickness 0.252 in | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 6.40 mm | 181 °F @Thickness 0.252 in | ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | B/50; ISO R306 |
| 94.0 °C | 201 °F | B/120; ISO R306 | |