- 熔體流動速率 [g/10min]: 55.0
- 缺口沖擊強度: 0.294
- 拉伸強度 [MPa]: 60.8
- 彎曲模量 [MPa]: 2.45
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Melt Flow | 55 g/10 min @Load 2.16 kg, Temperature 250 °C | 55 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 60.8 MPa | 8820 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.294 J/cm @Thickness 3.17 mm | 0.551 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 180 °C | 356 °F | B/50; ISO R306 |
| Optical Properties | Metric | English | Comments |
| Gloss | >= 92 % @Temperature 23.0 °C | >= 92 % @Temperature 73.4 °F | 50% RH, 60°; ASTM D2457 |