- 熔體流動(dòng)速率 [g/10min]: 21.0
- 缺口沖擊強(qiáng)度: 1.77
- 拉伸強(qiáng)度 [MPa]: 56.9
- 彎曲模量 [MPa]: 2.45
- 硬度: 111.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm | 0.0030 - 0.0050 in/in @Thickness 0.126 in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | ASTM D955 |
| Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 260 °C | 21 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 81.4 MPa | 11800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.77 J/cm @Thickness 6.35 mm | 3.31 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| 5.49 J/cm @Thickness 3.17 mm | 10.3 ft-lb/in @Thickness 0.125 in | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 6.40 mm | 226 °F @Thickness 0.252 in | ASTM D648 |
| Vicat Softening Point | 135 °C | 275 °F | B/50; ISO R306 |