- 熔體流動速率 [g/10min]: 32.4
- 缺口沖擊強度: 7.06
- 拉伸強度 [MPa]: 55.9
- 彎曲模量 [MPa]: 2.06
- 硬度: 116.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Melt Flow | 32.4 g/10 min @Load 10.0 kg, Temperature 250 °C | 32.4 g/10 min @Load 22.0 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Yield | 55.9 MPa | 8110 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 76.5 MPa | 11100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 7.06 J/cm @Thickness 3.17 mm | 13.2 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C @Thickness 6.40 mm | 225 °F @Thickness 0.252 in | ASTM D648 |
| Vicat Softening Point | 131 °C | 268 °F | B/50; ISO R306 |