- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.18
- 缺口沖擊強度: 9.0
- 拉伸強度 [MPa]: 55.0
- 斷裂伸長率 [%]: 84.0
- 彎曲模量 [MPa]: 1.96
- 熱變形溫度 [℃]: 96.0
- 透光率 [%]: 88.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 265 °C | 12 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D 1238 |
| 12 g/10 min @Load 2.16 kg, Temperature 265 °C | 12 g/10 min @Load 4.76 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75 | 75 | 10S reading; ASTM D 2240 |
| Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D 638 |
| 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D 638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 135 % | 135 % | Type I, 50 mm/min; ASTM D 638 |
| >= 150 % | >= 150 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 1.88 GPa | 273 ksi | 50 mm/min; ASTM D 638 |
| 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 75.0 MPa | 10900 psi | break, 2 mm/min; ISO 178 |
| Flexural Yield Strength | 84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 9.00 J/cm @Temperature 23.0 °C | 16.9 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 @Temperature -10.0 °C | 2.38 ft-lb/in2 @Temperature 14.0 °F | 80*10*4; ISO 180/1A |
| 8.00 kJ/m2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |
| Impact Test | 95.0 J @Temperature 23.0 °C | 70.1 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D 257 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D 257 |
| Comparative Tracking Index | >= 600 V | >= 600 V | PLC code 0; UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 80.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 44.4 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| 105 μm/m-°C @Temperature -40.0 - 40.0 °C | 58.3 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 44.4 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| 105 μm/m-°C @Temperature -40.0 - 40.0 °C | 58.3 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft2-°F | ISO 8302 |
| Hot Ball Pressure Test | <= 105 °C | <= 221 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C @Thickness 3.20 mm | 205 °F @Thickness 0.126 in | unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 90.0 °C @Thickness 3.20 mm | 194 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Vicat Softening Point | 115 °C | 239 °F | Rate B/50; ASTM D 1525 |
| 115 °C | 239 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | UL 94 |
| Glow Wire Test | 750 °C @Thickness 1.00 mm | 1380 °F @Thickness 0.0394 in | Glow Wire Flammability Index; IEC 60695-2-12 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.557 | 1.557 | ISO 489 |
| Haze | 1.1 % @Thickness 2.54 mm | 1.1 % @Thickness 0.100 in | ASTM D 1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm | 88 % @Thickness 0.100 in | ASTM D 1003 |