- 熔體流動速率 [g/10min]: 30.0
- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.7
- 缺口沖擊強(qiáng)度: 7.0
- 拉伸強(qiáng)度 [MPa]: 52.0
- 斷裂伸長率 [%]: 95.0
- 彎曲模量 [MPa]: 2.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.70 % @Temperature 23.0 °C | 0.70 % @Temperature 73.4 °F | ISO 62 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 265 °C | 30 g/10 min @Load 4.76 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.70 GPa | 392 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A |
| 8.00 kJ/m2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 80.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 44.4 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 44.4 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| 80.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 44.4 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 130 °C | 266 °F | Rate B/50; ISO 306 |
| 140 °C | 284 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 0.000 mm | HB @Thickness 0.000 in | UL 94 |
| HB @Thickness 0.000 mm | HB @Thickness 0.000 in | UL 94 by SABIC-IP | |
| V-2 @Thickness 0.000 mm | V-2 @Thickness 0.000 in | UL 94 by SABIC-IP | |
| V-2 @Thickness 0.000 mm | V-2 @Thickness 0.000 in | UL 94 | |
| V-1 @Thickness 0.000 mm | V-1 @Thickness 0.000 in | UL 94 | |
| V-1 @Thickness 0.000 mm | V-1 @Thickness 0.000 in | UL 94 by SABIC-IP | |
| V-0 @Thickness 1.00 mm | V-0 @Thickness 0.0394 in | UL 94 by SABIC-IP | |
| V-0 @Thickness 1.00 mm | V-0 @Thickness 0.0394 in | UL 94 | |
| Glow Wire Test | 775 °C @Thickness 1.00 mm | 1430 °F @Thickness 0.0394 in | Glow Wire Ignitability Temperature; IEC 60695-2-13 |
| 775 °C @Thickness 2.00 mm | 1430 °F @Thickness 0.0787 in | Glow Wire Ignitability Temperature; IEC 60695-2-13 | |
| 775 °C @Thickness 3.00 mm | 1430 °F @Thickness 0.118 in | Glow Wire Ignitability Temperature; IEC 60695-2-13 | |