- 熔體流動速率 [g/10min]: 9.5
- 缺口沖擊強度: 0.883
- 拉伸強度 [MPa]: 142.0
- 彎曲模量 [MPa]: 13.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.75 g/cc | 1.75 g/cc | ASTM D792 |
| Melt Flow | 9.5 g/10 min @Load 2.16 kg, Temperature 250 °C | 9.5 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 142 MPa | 20600 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 216 MPa | 31300 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 13.7 GPa | 1990 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 6.35 mm | 1.65 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| 1.08 J/cm @Thickness 3.17 mm | 2.02 ft-lb/in @Thickness 0.125 in | ASTM D256 | |
| Izod Impact, Unnotched | 6.37 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 11.9 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C @Thickness 6.40 mm | 401 °F @Thickness 0.252 in | ASTM D648 |