- 熔體流動速率 [g/10min]: 21.0
- 密度 [g/cm3]: 1.18
- 缺口沖擊強度: 6.6
- 拉伸強度 [MPa]: 49.0
- 斷裂伸長率 [%]: 83.0
- 彎曲模量 [MPa]: 1.94
- 熱變形溫度 [℃]: 93.0
- 透光率 [%]: 88.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 265 °C | 21 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D 1238 |
| 21 g/10 min @Load 2.16 kg, Temperature 265 °C | 21 g/10 min @Load 4.76 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D 638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D 638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 150 % | 150 % | Type I, 50 mm/min; ASTM D 638 |
| >= 150 % | >= 150 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 1.84 GPa | 267 ksi | 50 mm/min; ASTM D 638 |
| 1.90 GPa | 276 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 71.0 MPa | 10300 psi | break, 2 mm/min; ISO 178 |
| Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 1.94 GPa | 281 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 6.60 J/cm @Temperature 23.0 °C | 12.4 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Impact Test | 95.0 J @Temperature 23.0 °C | 70.1 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 85.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 47.2 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| 115 μm/m-°C @Temperature -40.0 - 40.0 °C | 63.9 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 85.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 47.2 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| 105 μm/m-°C @Temperature -40.0 - 40.0 °C | 58.3 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C @Thickness 3.20 mm | 199 °F @Thickness 0.126 in | unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 88.0 °C @Thickness 3.20 mm | 190 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Vicat Softening Point | 106 °C | 223 °F | Rate B/120; ISO 306 |
| 108 °C | 226 °F | Rate B/50; ASTM D 1525 | |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % @Thickness 2.54 mm | 2.0 % @Thickness 0.100 in | ASTM D 1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm | 88 % @Thickness 0.100 in | ASTM D 1003 |