- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.7
- 缺口沖擊強度: 15.0
- 拉伸強度 [MPa]: 55.0
- 斷裂伸長率 [%]: 80.0
- 彎曲模量 [MPa]: 2.20
- 熱變形溫度 [℃]: 125.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.70 % @Temperature 23.0 °C | 0.70 % @Temperature 73.4 °F | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | on tensile bar; SABIC Method | ||
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | on tensile bar; SABIC Method | ||
| Melt Flow | 4.0 g/10 min @Load 1.20 kg, Temperature 265 °C | 4.0 g/10 min @Load 2.65 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, H358/30 | 95.0 MPa | 13800 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | ||
| Elongation at Break | 70 % | 70 % | 50 mm/min; ISO 527 | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 | ||
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 | ||
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 15.0 kJ/m2 @Temperature -40.0 °C | 7.14 ft-lb/in2 @Temperature -40.0 °F | 80*10*4; ISO 180/1A | ||
| 25.0 kJ/m2 @Temperature -30.0 °C | 11.9 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |||
| 35.0 kJ/m2 @Temperature -20.0 °C | 16.7 ft-lb/in2 @Temperature -4.00 °F | 80*10*4; ISO 180/1A | |||
| 38.0 kJ/m2 @Temperature -10.0 °C | 18.1 ft-lb/in2 @Temperature 14.0 °F | 80*10*4; ISO 180/1A | |||
| 40.0 kJ/m2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*4; ISO 180/1U | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 80*10*4; ISO 180/1U | |||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ISO 179/2C | ||
| 1.00 J/cm2 @Temperature -20.0 °C | 4.76 ft-lb/in2 @Temperature -4.00 °F | ISO 179/2C | |||
| 3.50 J/cm2 @Temperature -30.0 °C | 16.7 ft-lb/in2 @Temperature -22.0 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |||
| 4.50 J/cm2 @Temperature 23.0 °C | 21.4 ft-lb/in2 @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |||
| 5.00 J/cm2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/2C | |||
| Taber Abrasion, mg/1000 Cycles | 20 @Load 1.00 kg | 20 @Load 2.20 lb | CS-17; SABIC Method | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz | 3.1 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.3 @Frequency 50.0 - 60.0 Hz | 3.3 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |||
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm | 432 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | ||
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz | 0.0020 @Frequency 50.0 - 60.0 Hz | IEC 60250 | ||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 75.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 41.7 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 44.4 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| Thermal Conductivity | 0.180 W/m-K | 1.25 BTU-in/hr-ft2-°F | ISO 8302 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | ||
| Vicat Softening Point | 130 °C | 266 °F | Rate B/50; ISO 306 | ||
| 135 °C | 275 °F | Rate B/120; ISO 306 | |||
| 140 °C | 284 °F | Rate A/50; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 by SABIC-IP | ||
| Glow Wire Test | 750 °C @Thickness 2.70 mm | 1380 °F @Thickness 0.106 in | Glow Wire Flammability Index; IEC 60695-2-12 | ||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 | |||