- 熔體流動(dòng)速率 [g/10min]: 35.0
- 缺口沖擊強(qiáng)度: 2.06
- 拉伸強(qiáng)度 [MPa]: 38.2
- 彎曲模量 [MPa]: 1.96
- 硬度: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0070 in/in @Thickness 0.126 in | ASTM D955 |
| Melt Flow | 35 g/10 min @Load 10.0 kg, Temperature 250 °C | 35 g/10 min @Load 22.0 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 38.2 MPa | 5550 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 55.9 MPa | 8110 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.06 J/cm @Thickness 3.17 mm | 3.86 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C @Thickness 6.40 mm | 172 °F @Thickness 0.252 in | ASTM D648 |
| Vicat Softening Point | 88.0 °C | 190 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm | HB @Thickness 0.0591 - 0.118 in | |
| Optical Properties | Metric | English | Comments |
| Yellow Index | 20 % @Thickness 3.20 mm | 20 % @Thickness 0.126 in | ASTM D1925 |