- 缺口沖擊強度: 2.94
- 拉伸強度 [MPa]: 39.2
- 彎曲模量 [MPa]: 1.81
- 硬度: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 39.2 MPa | 5690 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 51.0 MPa | 7400 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.81 GPa | 263 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.94 J/cm @Thickness 3.17 mm | 5.51 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 91.0 °C | 196 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm | HB @Thickness 0.0591 - 0.118 in | |