- 密度 [g/cm3]: 1.65
- 吸水率 [%]: 0.05
- 缺口沖擊強(qiáng)度: 0.66
- 斷裂伸長(zhǎng)率 [%]: 202
- 彎曲模量 [MPa]: 12.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in3 | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | (24 hr); ASTM D570 |
| Moisture Absorption at Equilibrium | 0.21 % | 0.21 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 129.6 MPa | 18800 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 202 MPa | 29300 psi | ASTM D790 |
| Flexural Modulus | 12.2 GPa | 1770 ksi | ASTM D790 |
| Izod Impact, Notched | 0.660 J/cm | 1.24 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 0.032 in; Albis Internal test |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 257 - 277 °C | 495 - 531 °F | Injection |
| Mold Temperature | 91.0 - 121 °C | 196 - 250 °F | |