- 熔體流動(dòng)速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 0.06
- 缺口沖擊強(qiáng)度: 0.412
- 斷裂伸長(zhǎng)率 [%]: 63.7
- 彎曲強(qiáng)度 [MPa]: 58.8
- 彎曲模量 [MPa]: 2.16
- 硬度: 88.0
- 熱變形溫度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 - 1.45 g/cc | 0.0480 - 0.0524 lb/in3 | Average value: 1.35 g/cc Grade Count:6 |
| Water Absorption | 0.0600 - 0.150 % | 0.0600 - 0.150 % | Average value: 0.0800 % Grade Count:6 |
| Linear Mold Shrinkage | 0.00400 - 0.0150 cm/cm | 0.00400 - 0.0150 in/in | Average value: 0.00667 cm/cm Grade Count:6 |
| Melt Flow | 12.0 - 25.0 g/10 min | 12.0 - 25.0 g/10 min | Average value: 16.4 g/10 min Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 88.0 - 115 | 88.0 - 115 | Average value: 96.7 Grade Count:6 |
| Tensile Strength, Ultimate | 58.8 - 81.4 MPa | 8530 - 11800 psi | Average value: 68.7 MPa Grade Count:6 |
| Elongation at Break | 40.0 - 460 % | 40.0 - 460 % | Average value: 187 % Grade Count:6 |
| Flexural Yield Strength | 63.7 - 92.2 MPa | 9250 - 13400 psi | Average value: 85.4 MPa Grade Count:6 |
| Flexural Modulus | 2.16 - 3.14 GPa | 313 - 455 ksi | Average value: 2.63 GPa Grade Count:6 |
| Izod Impact, Notched | 0.412 - 0.539 J/cm | 0.772 - 1.01 ft-lb/in | Average value: 0.461 J/cm Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 - 400 μm/m-°C | 33.3 - 222 μin/in-°F | Average value: 117 μm/m-°C Grade Count:6 |
| Melting Point | 215 - 255 °C | 419 - 491 °F | Average value: 240 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 - 120 °C | 167 - 248 °F | Average value: 96.5 °C Grade Count:6 |
| Glass Transition Temp, Tg | 82.0 - 121 °C | 180 - 250 °F | Average value: 98.8 °C Grade Count:5 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:6 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.00 - 1.60 % | 1.00 - 1.60 % | Average value: 1.22 % Grade Count:5 |
- 關(guān)鍵詞:
- PET
- 供應(yīng)
- Overview of materials for PEN-PET