- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 0.38
- 斷裂伸長率 [%]: 100
- 彎曲強度 [MPa]: 65.0
- 彎曲模量 [MPa]: 3.70
- 熱變形溫度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 - 1.72 g/cc | 0.0452 - 0.0621 lb/in3 | Average value: 1.55 g/cc Grade Count:6 |
| Water Absorption | 0.0600 - 0.0900 % | 0.0600 - 0.0900 % | Average value: 0.0750 % Grade Count:4 |
| Linear Mold Shrinkage | 0.00200 - 0.0140 cm/cm | 0.00200 - 0.0140 in/in | Average value: 0.00550 cm/cm Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 65.0 - 140 MPa | 9430 - 20300 psi | Average value: 102 MPa Grade Count:6 |
| Elongation at Break | 1.40 - 8.00 % | 1.40 - 8.00 % | Average value: 2.89 % Grade Count:6 |
| Flexural Yield Strength | 100 - 215 MPa | 14500 - 31200 psi | Average value: 158 MPa Grade Count:6 |
| Flexural Modulus | 3.70 - 15.6 GPa | 537 - 2260 ksi | Average value: 9.65 GPa Grade Count:6 |
| Izod Impact, Notched | 0.380 - 0.700 J/cm | 0.712 - 1.31 ft-lb/in | Average value: 0.570 J/cm Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.20 - 3.90 | 3.20 - 3.90 | Average value: 3.65 Grade Count:4 |
| Dielectric Strength | 17.0 - 28.0 kV/mm | 432 - 711 kV/in | Average value: 20.6 kV/mm Grade Count:5 |
| 13.8 - 25.6 kV/mm @Temperature 120 - 200 °C | 351 - 650 kV/in @Temperature 248 - 392 °F | Average value: 19.7 kV/mm Grade Count:1 | |
| 13.8 - 25.6 kV/mm @Thickness 3.20 - 3.20 mm | 351 - 650 kV/in @Thickness 0.126 - 0.126 in | Average value: 19.7 kV/mm Grade Count:1 | |
| Dissipation Factor | 0.0100 - 0.0200 | 0.0100 - 0.0200 | Average value: 0.0125 Grade Count:4 |
| Arc Resistance | 101 - 126 sec | 101 - 126 sec | Average value: 120 sec Grade Count:4 |
| Comparative Tracking Index | 200 - 250 V | 200 - 250 V | Average value: 217 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.6 - 37.8 μm/m-°C | 17.0 - 21.0 μin/in-°F | Average value: 32.4 μm/m-°C Grade Count:4 |
| 12.96 - 23.4 μm/m-°C @Temperature 100 - 100 °C | 7.200 - 13.0 μin/in-°F @Temperature 212 - 212 °F | Average value: 18.2 μm/m-°C Grade Count:2 | |
| CTE, linear, Transverse to Flow | 50.0 - 103 μm/m-°C | 27.8 - 57.2 μin/in-°F | Average value: 78.8 μm/m-°C Grade Count:4 |
| 66.6 - 84.6 μm/m-°C @Temperature 100 - 100 °C | 37.0 - 47.0 μin/in-°F @Temperature 212 - 212 °F | Average value: 75.6 μm/m-°C Grade Count:2 | |
| Melting Point | 248 - 260 °C | 478 - 500 °F | Average value: 252 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 - 245 °C | 433 - 473 °F | Average value: 236 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 - 228 °C | 212 - 442 °F | Average value: 193 °C Grade Count:6 |
| Flammability, UL94 | HB | HB | Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 280 °C | 518 - 536 °F | Average value: 275 °C Grade Count:4 |