- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.35
- 拉伸強度 [MPa]: 75.0
- 斷裂伸長率 [%]: 110
- 彎曲強度 [MPa]: 70.0
- 彎曲模量 [MPa]: 4.12
- 硬度: 110.0
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 - 1.76 g/cc | 0.0493 - 0.0636 lb/in3 | Average value: 1.56 g/cc Grade Count:69 |
| Filler Content | 15.0 - 30.0 % | 15.0 - 30.0 % | Average value: 22.5 % Grade Count:4 |
| Water Absorption | 0.300 - 0.400 % | 0.300 - 0.400 % | Average value: 0.368 % Grade Count:17 |
| Moisture Absorption at Equilibrium | 0.0300 - 0.200 % | 0.0300 - 0.200 % | Average value: 0.118 % Grade Count:43 |
| Water Absorption at Saturation | 0.150 - 0.500 % | 0.150 - 0.500 % | Average value: 0.242 % Grade Count:20 |
| Viscosity | 145000 - 195000 cP | 145000 - 195000 cP | Average value: 164000 cP Grade Count:4 |
| Viscosity Measurement | 90.0 - 107 | 90.0 - 107 | Average value: 102 Grade Count:4 |
| 70.0 - 120 @Temperature 240 - 300 °C | 70.0 - 120 @Temperature 464 - 572 °F | Average value: 99.5 Grade Count:2 | |
| Viscosity Test | 50.0 - 95.0 cm3/g | 50.0 - 95.0 cm3/g | Average value: 80.9 cm3/g Grade Count:16 |
| Maximum Moisture Content | 0.0200 | 0.0200 | Average value: 0.0200 Grade Count:5 |
| Linear Mold Shrinkage | 0.00100 - 0.0100 cm/cm | 0.00100 - 0.0100 in/in | Average value: 0.00417 cm/cm Grade Count:45 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0120 cm/cm | 0.00100 - 0.0120 in/in | Average value: 0.00705 cm/cm Grade Count:31 |
| Melt Flow | 5.00 - 130 g/10 min | 5.00 - 130 g/10 min | Average value: 28.1 g/10 min Grade Count:48 |
| Ash | 15.0 - 45.0 % | 15.0 - 45.0 % | Average value: 30.0 % Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 - 121 | 110 - 121 | Average value: 118 Grade Count:9 |
| Hardness, H358/30 | 101 - 234 MPa | 14600 - 33900 psi | Average value: 142 MPa Grade Count:10 |
| Ball Indentation Hardness | 180 - 250 MPa | 26100 - 36300 psi | Average value: 205 MPa Grade Count:4 |
| Tensile Strength, Ultimate | 70.0 - 175 MPa | 10200 - 25400 psi | Average value: 121 MPa Grade Count:63 |
| Tensile Strength, Yield | 75.0 - 175 MPa | 10900 - 25400 psi | Average value: 116 MPa Grade Count:23 |
| Elongation at Break | 1.10 - 90.0 % | 1.10 - 90.0 % | Average value: 3.51 % Grade Count:63 |
| Elongation at Yield | 1.00 - 140 % | 1.00 - 140 % | Average value: 6.39 % Grade Count:19 |
| Modulus of Elasticity | 5.00 - 19.0 GPa | 725 - 2760 ksi | Average value: 10.1 GPa Grade Count:57 |
| Flexural Yield Strength | 110 - 260 MPa | 16000 - 37700 psi | Average value: 176 MPa Grade Count:39 |
| Flexural Modulus | 4.12 - 16.2 GPa | 597 - 2350 ksi | Average value: 8.46 GPa Grade Count:40 |
| Izod Impact, Notched | 0.350 - 1.08 J/cm | 0.656 - 2.02 ft-lb/in | Average value: 0.683 J/cm Grade Count:28 |
| 0.300 - 0.850 J/cm @Temperature -30.0 - 0.000 °C | 0.562 - 1.59 ft-lb/in @Temperature -22.0 - 32.0 °F | Average value: 0.547 J/cm Grade Count:13 | |
| Izod Impact, Unnotched | 2.50 - 8.20 J/cm | 4.68 - 15.4 ft-lb/in | Average value: 4.92 J/cm Grade Count:11 |
| 2.80 - 7.45 J/cm @Temperature -30.0 - -30.0 °C | 5.25 - 14.0 ft-lb/in @Temperature -22.0 - -22.0 °F | Average value: 4.67 J/cm Grade Count:8 | |
| Izod Impact, Notched (ISO) | 4.00 - 11.0 kJ/m2 | 1.90 - 5.23 ft-lb/in2 | Average value: 8.26 kJ/m2 Grade Count:31 |
| 4.00 - 10.0 kJ/m2 @Temperature -40.0 - 0.000 °C | 1.90 - 4.76 ft-lb/in2 @Temperature -40.0 - 32.0 °F | Average value: 7.70 kJ/m2 Grade Count:29 | |
| Izod Impact, Unnotched (ISO) | 22.0 - 65.0 kJ/m2 | 10.5 - 30.9 ft-lb/in2 | Average value: 39.9 kJ/m2 Grade Count:23 |
| 20.0 - 60.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 9.52 - 28.6 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 38.7 kJ/m2 Grade Count:21 | |
| Charpy Impact Unnotched | 2.30 - 7.00 J/cm2 | 10.9 - 33.3 ft-lb/in2 | Average value: 4.57 J/cm2 Grade Count:37 |
| 2.00 - 7.00 J/cm2 @Temperature -30.0 - -30.0 °C | 9.52 - 33.3 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 4.32 J/cm2 Grade Count:31 | |
| Charpy Impact, Notched | 0.380 - 2.30 J/cm2 | 1.81 - 10.9 ft-lb/in2 | Average value: 0.892 J/cm2 Grade Count:42 |
| 0.400 - 1.20 J/cm2 @Temperature -30.0 - -20.0 °C | 1.90 - 5.71 ft-lb/in2 @Temperature -22.0 - -4.00 °F | Average value: 0.903 J/cm2 Grade Count:27 | |
| Dart Drop, Total Energy | 5.00 - 8.00 J | 3.69 - 5.90 ft-lb | Average value: 6.75 J Grade Count:12 |
| Puncture Energy | 2.10 - 3.50 J | 1.55 - 2.58 ft-lb | Average value: 2.50 J Grade Count:5 |
| 1.80 - 1.80 J @Temperature -30.0 - -30.0 °C | 1.33 - 1.33 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 1.80 J Grade Count:1 | |
| Tensile Creep Modulus, 1 hour | 7200 - 16500 MPa | 1.04e+6 - 2.39e+6 psi | Average value: 11700 MPa Grade Count:8 |
| Tensile Creep Modulus, 1000 hours | 6100 - 15000 MPa | 885000 - 2.18e+6 psi | Average value: 10300 MPa Grade Count:8 |
| Taber Abrasion, mg/1000 Cycles | 17.0 - 45.0 | 17.0 - 45.0 | Average value: 30.3 Grade Count:6 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 2.00e+20 ohm-cm | 1.00e+13 - 2.00e+20 ohm-cm | Average value: 1.21e+19 ohm-cm Grade Count:31 |
| Surface Resistance | 1.00e+13 - 5.40e+16 ohm | 1.00e+13 - 5.40e+16 ohm | Average value: 4.62e+15 ohm Grade Count:30 |
| Dielectric Constant | 2.90 - 4.70 | 2.90 - 4.70 | Average value: 3.78 Grade Count:27 |
| Dielectric Strength | 8.00 - 38.0 kV/mm | 203 - 965 kV/in | Average value: 24.1 kV/mm Grade Count:25 |
| Dissipation Factor | 0.000800 - 0.0200 | 0.000800 - 0.0200 | Average value: 0.00864 Grade Count:25 |
| Comparative Tracking Index | 175 - 600 V | 175 - 600 V | Average value: 278 V Grade Count:34 |
| Hot Wire Ignition, HWI | 120 sec | 120 sec | Average value: 120 sec Grade Count:3 |
| High Amp Arc Ignition, HAI | 120 arcs | 120 arcs | Average value: 120 arcs Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.200 - 55.0 μm/m-°C | 0.111 - 30.6 μin/in-°F | Average value: 28.6 μm/m-°C Grade Count:40 |
| CTE, linear, Transverse to Flow | 50.0 - 165 μm/m-°C | 27.8 - 91.7 μin/in-°F | Average value: 80.4 μm/m-°C Grade Count:37 |
| Thermal Conductivity | 0.190 - 0.320 W/m-K | 1.32 - 2.22 BTU-in/hr-ft2-°F | Average value: 0.270 W/m-K Grade Count:5 |
| Melting Point | 220 - 260 °C | 428 - 500 °F | Average value: 236 °C Grade Count:34 |
| Maximum Service Temperature, Air | 140 - 220 °C | 284 - 428 °F | Average value: 171 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 - 250 °C | 392 - 482 °F | Average value: 218 °C Grade Count:55 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 - 215 °C | 190 - 419 °F | Average value: 192 °C Grade Count:69 |
| Deflection Temperature at 8.0 MPa | 72.0 - 150 °C | 162 - 302 °F | Average value: 120 °C Grade Count:6 |
| Vicat Softening Point | 150 - 225 °C | 302 - 437 °F | Average value: 205 °C Grade Count:34 |
| Decomposition Temperature | 290 °C | 554 °F | Average value: 290 °C Grade Count:3 |
| UL RTI, Electrical | 75.0 - 140 °C | 167 - 284 °F | Average value: 92.1 °C Grade Count:7 |
| UL RTI, Mechanical with Impact | 75.0 - 130 °C | 167 - 266 °F | Average value: 90.0 °C Grade Count:7 |
| UL RTI, Mechanical without Impact | 75.0 - 140 °C | 167 - 284 °F | Average value: 93.6 °C Grade Count:7 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:41 |
| Oxygen Index | 21.0 - 31.0 % | 21.0 - 31.0 % | Average value: 22.3 % Grade Count:11 |
| Glow Wire Test | 725 - 960 °C | 1340 - 1760 °F | Average value: 805 °C Grade Count:9 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 280 °C | 176 - 536 °F | Average value: 205 °C Grade Count:9 |
| Feed Temperature | 50.0 - 270 °C | 122 - 518 °F | Average value: 128 °C Grade Count:9 |
| Nozzle Temperature | 255 - 290 °C | 491 - 554 °F | Average value: 268 °C Grade Count:8 |
| Melt Temperature | 225 - 300 °C | 437 - 572 °F | Average value: 265 °C Grade Count:35 |
| Mold Temperature | 60.0 - 150 °C | 140 - 302 °F | Average value: 89.9 °C Grade Count:41 |
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | Average value: 117 °C Grade Count:23 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 4.98 hour Grade Count:23 |
| Moisture Content | 0.000 - 0.0800 % | 0.000 - 0.0800 % | Average value: 0.0400 % Grade Count:15 |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi | Average value: 70.0 MPa Grade Count:3 |
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi | Average value: 60.0 MPa Grade Count:6 |