- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.27
- 缺口沖擊強度: 0.641
- 拉伸強度 [MPa]: 72.4
- 斷裂伸長率 [%]: 121
- 彎曲強度 [MPa]: 72.4
- 彎曲模量 [MPa]: 3.24
- 熱變形溫度 [℃]: 116.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 - 1.59 g/cc | 0.0459 - 0.0574 lb/in3 | Average value: 1.39 g/cc Grade Count:7 |
| Linear Mold Shrinkage | 0.00100 - 0.00800 cm/cm | 0.00100 - 0.00800 in/in | Average value: 0.00436 cm/cm Grade Count:7 |
| Melt Flow | 1.00 - 16.0 g/10 min | 1.00 - 16.0 g/10 min | Average value: 10.5 g/10 min Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 72.4 - 105 MPa | 10500 - 15200 psi | Average value: 87.9 MPa Grade Count:4 |
| Tensile Strength, Yield | 72.4 - 103 MPa | 10500 - 14900 psi | Average value: 88.7 MPa Grade Count:4 |
| Flexural Yield Strength | 121 - 170 MPa | 17500 - 24700 psi | Average value: 142 MPa Grade Count:4 |
| Flexural Modulus | 3.24 - 6.76 GPa | 469 - 980 ksi | Average value: 4.96 GPa Grade Count:7 |
| Izod Impact, Notched | 0.641 - 7.85 J/cm | 1.20 - 14.7 ft-lb/in | Average value: 2.94 J/cm Grade Count:7 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 - 204 °C | 240 - 400 °F | Average value: 149 °C Grade Count:5 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 - 135 °C | 230 - 275 °F | Average value: 120 °C Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 254 - 296 °C | 490 - 565 °F | Average value: 275 °C Grade Count:3 |
| Mold Temperature | 65.6 - 116 °C | 150 - 241 °F | Average value: 84.2 °C Grade Count:3 |
| Dry Time | 2.00 - 4.00 hour @Temperature 121 - 121 °C | 2.00 - 4.00 hour @Temperature 250 - 250 °F | Average value: 3.00 hour Grade Count:1 |