- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.04
- 缺口沖擊強度: 1.07
- 斷裂伸長率 [%]: 256.5
- 彎曲模量 [MPa]: 14.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in3 | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | (24 hr); ASTM D570 |
| Moisture Absorption at Equilibrium | 0.21 % | 0.21 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 173.1 MPa | 25110 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 256.5 MPa | 37200 psi | ASTM D790 |
| Flexural Modulus | 14.2 GPa | 2060 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 226 °C | 439 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 0.032 in; Albis Internal test |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 257 - 277 °C | 495 - 531 °F | Injection |
| Mold Temperature | 91.0 - 121 °C | 196 - 250 °F | |