- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 0.05
- 缺口沖擊強度: 0.587
- 拉伸強度 [MPa]: 110.0
- 斷裂伸長率 [%]: 120
- 彎曲強度 [MPa]: 78.6
- 彎曲模量 [MPa]: 5.52
- 硬度: 111.0
- 熱變形溫度 [℃]: 230.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 - 1.80 g/cc | 0.0538 - 0.0650 lb/in3 | Average value: 1.64 g/cc Grade Count:28 |
| Water Absorption | 0.0500 - 0.150 % | 0.0500 - 0.150 % | Average value: 0.0843 % Grade Count:14 |
| Linear Mold Shrinkage | 0.00100 - 0.0110 cm/cm | 0.00100 - 0.0110 in/in | Average value: 0.00338 cm/cm Grade Count:28 |
| Linear Mold Shrinkage, Transverse | 0.00300 - 0.0100 cm/cm | 0.00300 - 0.0100 in/in | Average value: 0.00827 cm/cm Grade Count:11 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90.0 - 95.0 | 90.0 - 95.0 | Average value: 93.5 Grade Count:6 |
| Hardness, Rockwell R | 111 - 120 | 111 - 120 | Average value: 118 Grade Count:10 |
| Tensile Strength, Ultimate | 78.6 - 172 MPa | 11400 - 24900 psi | Average value: 127 MPa Grade Count:23 |
| 50.0 - 170 MPa @Temperature -40.0 - 120 °C | 7250 - 24700 psi @Temperature -40.0 - 248 °F | Average value: 101 MPa Grade Count:2 | |
| Tensile Strength, Yield | 110 - 157 MPa | 16000 - 22800 psi | Average value: 139 MPa Grade Count:5 |
| Elongation at Break | 0.500 - 6.00 % | 0.500 - 6.00 % | Average value: 2.41 % Grade Count:26 |
| 1.70 - 5.70 % @Temperature -40.0 - 120 °C | 1.70 - 5.70 % @Temperature -40.0 - 248 °F | Average value: 3.92 % Grade Count:2 | |
| Modulus of Elasticity | 6.21 - 14.6 GPa | 900 - 2120 ksi | Average value: 11.0 GPa Grade Count:6 |
| 3.71 - 12.5 GPa @Temperature -40.0 - 120 °C | 538 - 1810 ksi @Temperature -40.0 - 248 °F | Average value: 7.42 GPa Grade Count:1 | |
| Flexural Yield Strength | 120 - 278 MPa | 17400 - 40300 psi | Average value: 191 MPa Grade Count:24 |
| 85.0 - 275 MPa @Temperature -40.0 - 120 °C | 12300 - 39900 psi @Temperature -40.0 - 248 °F | Average value: 180 MPa Grade Count:1 | |
| Flexural Modulus | 5.52 - 16.0 GPa | 800 - 2320 ksi | Average value: 9.69 GPa Grade Count:28 |
| 2.97 - 2.97 GPa @Temperature 120 - 120 °C | 431 - 431 ksi @Temperature 248 - 248 °F | Average value: 2.97 GPa Grade Count:1 | |
| Compressive Yield Strength | 98.0 - 128 MPa | 14200 - 18600 psi | Average value: 110 MPa Grade Count:5 |
| Izod Impact, Notched | 0.587 - 1.60 J/cm | 1.10 - 3.00 ft-lb/in | Average value: 0.891 J/cm Grade Count:25 |
| 0.800 - 0.800 J/cm @Temperature -40.0 - -40.0 °C | 1.50 - 1.50 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.800 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 0.834 - 8.70 J/cm | 1.56 - 16.3 ft-lb/in | Average value: 3.24 J/cm Grade Count:6 |
| Izod Impact, Notched (ISO) | 11.5 - 11.5 kJ/m2 @Temperature -40.0 - -40.0 °C | 5.47 - 5.47 ft-lb/in2 @Temperature -40.0 - -40.0 °F | Average value: 11.5 kJ/m2 Grade Count:1 |
| Charpy Impact, Notched | 1.40 - 1.40 J/cm2 @Temperature -30.0 - -30.0 °C | 6.66 - 6.66 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 1.40 J/cm2 Grade Count:1 |
| Taber Abrasion, mg/1000 Cycles | 25.0 - 36.0 | 25.0 - 36.0 | Average value: 30.6 Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 1.00e+18 ohm-cm | 1.00e+13 - 1.00e+18 ohm-cm | Average value: 6.01e+16 ohm-cm Grade Count:19 |
| Dielectric Constant | 3.60 - 4.00 | 3.60 - 4.00 | Average value: 3.85 Grade Count:8 |
| Dielectric Strength | 20.0 - 40.0 kV/mm | 508 - 1020 kV/in | Average value: 26.0 kV/mm Grade Count:14 |
| Dissipation Factor | 0.0100 - 0.0200 | 0.0100 - 0.0200 | Average value: 0.0174 Grade Count:5 |
| Arc Resistance | 80.0 - 85.0 sec | 80.0 - 85.0 sec | Average value: 82.3 sec Grade Count:7 |
| Comparative Tracking Index | 0.000 - 260 V | 0.000 - 260 V | Average value: 172 V Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 22.0 - 30.0 μm/m-°C | 12.2 - 16.7 μin/in-°F | Average value: 25.7 μm/m-°C Grade Count:5 |
| Melting Point | 245 - 255 °C | 473 - 491 °F | Average value: 251 °C Grade Count:17 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 - 245 °C | 446 - 473 °F | Average value: 240 °C Grade Count:15 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 - 228 °C | 383 - 442 °F | Average value: 217 °C Grade Count:24 |
| UL RTI, Electrical | 130 °C | 266 °F | Average value: 130 °C Grade Count:5 |
| Flammability, UL94 | V-0 - 5VA | V-0 - 5VA | Grade Count:25 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 243 - 293 °C | 470 - 560 °F | Average value: 272 °C Grade Count:5 |
| Melt Temperature | 235 - 295 °C | 455 - 563 °F | Average value: 266 °C Grade Count:8 |
| Mold Temperature | 80.0 - 163 °C | 176 - 325 °F | Average value: 115 °C Grade Count:12 |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | Average value: 126 °C Grade Count:5 |
| Injection Pressure | 55.0 - 103 MPa | 7980 - 15000 psi | Average value: 75.4 MPa Grade Count:3 |