- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.04
- 缺口沖擊強度: 0.49
- 拉伸強度 [MPa]: 0.971
- 斷裂伸長率 [%]: 90.0
- 彎曲強度 [MPa]: 22.7
- 彎曲模量 [MPa]: 3.65
- 硬度: 115.0
- 熱變形溫度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 - 1.75 g/cc | 0.0477 - 0.0632 lb/in3 | Average value: 1.59 g/cc Grade Count:66 |
| Filler Content | 30.0 % | 30.0 % | Average value: 30.0 % Grade Count:14 |
| Water Absorption | 0.0400 - 0.770 % | 0.0400 - 0.770 % | Average value: 0.207 % Grade Count:21 |
| Moisture Absorption at Equilibrium | 0.0500 - 0.240 % | 0.0500 - 0.240 % | Average value: 0.171 % Grade Count:17 |
| Viscosity | 32000 - 4.11e+6 cP @Temperature 275 - 305 °C | 32000 - 4.11e+6 cP @Temperature 527 - 581 °F | Average value: 513000 cP Grade Count:3 |
| 32000 - 4.11e+6 cP @Shear Rate 7.30 - 7000 1/s | 32000 - 4.11e+6 cP @Shear Rate 7.30 - 7000 1/s | Average value: 513000 cP Grade Count:3 | |
| Viscosity Measurement | 0.550 | 0.550 | Average value: 0.550 Grade Count:3 |
| Linear Mold Shrinkage | 0.00100 - 0.0110 cm/cm | 0.00100 - 0.0110 in/in | Average value: 0.00343 cm/cm Grade Count:59 |
| Linear Mold Shrinkage, Transverse | 0.00300 - 0.0125 cm/cm | 0.00300 - 0.0125 in/in | Average value: 0.00831 cm/cm Grade Count:30 |
| Melt Flow | 5.00 - 65.0 g/10 min | 5.00 - 65.0 g/10 min | Average value: 14.8 g/10 min Grade Count:7 |
| Ash | 30.0 - 84.0 % | 30.0 - 84.0 % | Average value: 49.7 % Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 70.0 - 123 | 70.0 - 123 | Average value: 98.8 Grade Count:13 |
| Hardness, Rockwell R | 115 - 122 | 115 - 122 | Average value: 119 Grade Count:20 |
| Tensile Strength, Ultimate | 22.7 - 170 MPa | 3290 - 24700 psi | Average value: 124 MPa Grade Count:51 |
| 43.0 - 214 MPa @Temperature -40.0 - 150 °C | 6240 - 31000 psi @Temperature -40.0 - 302 °F | Average value: 77.4 MPa Grade Count:7 | |
| 16.0 - 211 MPa @Temperature -40.0 - 150 °C | 2320 - 30600 psi @Temperature -40.0 - 302 °F | Average value: 77.4 MPa Grade Count:4 | |
| 16.0 - 211 MPa @Strain 0.180 - 10.5 % | 2320 - 30600 psi @Strain 0.180 - 10.5 % | Average value: 77.4 MPa Grade Count:4 | |
| Tensile Strength, Yield | 0.971 - 162 MPa | 141 - 23500 psi | Average value: 118 MPa Grade Count:15 |
| Elongation at Break | 1.50 - 6.60 % | 1.50 - 6.60 % | Average value: 2.57 % Grade Count:56 |
| 1.80 - 11.0 % @Temperature -40.0 - 150 °C | 1.80 - 11.0 % @Temperature -40.0 - 302 °F | Average value: 4.60 % Grade Count:6 | |
| Modulus of Elasticity | 4.27 - 13.5 GPa | 620 - 1960 ksi | Average value: 10.5 GPa Grade Count:32 |
| 2.70 - 12.5 GPa @Temperature -40.0 - 150 °C | 392 - 1810 ksi @Temperature -40.0 - 302 °F | Average value: 6.62 GPa Grade Count:6 | |
| Flexural Yield Strength | 90.0 - 270 MPa | 13100 - 39200 psi | Average value: 206 MPa Grade Count:48 |
| 60.0 - 275 MPa @Temperature -40.0 - 150 °C | 8700 - 39900 psi @Temperature -40.0 - 302 °F | Average value: 156 MPa Grade Count:5 | |
| Flexural Modulus | 3.65 - 11.4 GPa | 530 - 1650 ksi | Average value: 9.29 GPa Grade Count:51 |
| 2.25 - 11.0 GPa @Temperature -40.0 - 150 °C | 326 - 1600 ksi @Temperature -40.0 - 302 °F | Average value: 5.45 GPa Grade Count:7 | |
| Compressive Yield Strength | 148 - 233 MPa | 21500 - 33800 psi | Average value: 192 MPa Grade Count:6 |
| Shear Modulus | 0.162 - 2.11 GPa @Temperature -50.0 - 250 °C | 23.5 - 306 ksi @Temperature -58.0 - 482 °F | Average value: 0.996 GPa Grade Count:1 |
| Izod Impact, Notched | 0.490 - 1.82 J/cm | 0.919 - 3.40 ft-lb/in | Average value: 0.891 J/cm Grade Count:44 |
| 0.800 - 1.01 J/cm @Temperature -40.0 - -40.0 °C | 1.50 - 1.89 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.923 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 0.883 - 9.60 J/cm | 1.65 - 18.0 ft-lb/in | Average value: 5.90 J/cm Grade Count:11 |
| 5.35 - 9.60 J/cm @Temperature -40.0 - -40.0 °C | 10.0 - 18.0 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 7.48 J/cm Grade Count:3 | |
| Izod Impact, Notched (ISO) | 7.00 - 18.0 kJ/m2 | 3.33 - 8.57 ft-lb/in2 | Average value: 9.67 kJ/m2 Grade Count:27 |
| 6.00 - 10.0 kJ/m2 @Temperature -40.0 - -30.0 °C | 2.86 - 4.76 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 7.89 kJ/m2 Grade Count:15 | |
| Izod Impact, Unnotched (ISO) | 30.0 - 60.0 kJ/m2 | 14.3 - 28.6 ft-lb/in2 | Average value: 41.3 kJ/m2 Grade Count:12 |
| 25.0 - 45.0 kJ/m2 @Temperature -40.0 - -30.0 °C | 11.9 - 21.4 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 34.4 kJ/m2 Grade Count:9 | |
| Charpy Impact Unnotched | 2.70 - 7.00 J/cm2 | 12.8 - 33.3 ft-lb/in2 | Average value: 4.65 J/cm2 Grade Count:13 |
| 2.80 - 8.60 J/cm2 @Temperature -40.0 - -30.0 °C | 13.3 - 40.9 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 4.18 J/cm2 Grade Count:10 | |
| Charpy Impact, Notched | 0.850 - 1.60 J/cm2 | 4.05 - 7.61 ft-lb/in2 | Average value: 1.05 J/cm2 Grade Count:15 |
| 0.800 - 1.20 J/cm2 @Temperature -40.0 - -30.0 °C | 3.81 - 5.71 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 0.914 J/cm2 Grade Count:11 | |
| Tensile Creep Modulus, 1 hour | 0.000 - 11200 MPa | 0.000 - 1.62e+6 psi | Average value: 928 MPa Grade Count:3 |
| 0.000 - 30.0 MPa @Temperature 100 - 100 °C | 0.000 - 4350 psi @Temperature 212 - 212 °F | Average value: 15.0 MPa Grade Count:1 | |
| 0.000 - 30.0 MPa @Strain 0.000 - 1.04 % | 0.000 - 4350 psi @Strain 0.000 - 1.04 % | Average value: 15.0 MPa Grade Count:1 | |
| Tensile Creep Modulus, 1000 hours | 0.000 - 9700 MPa | 0.000 - 1.41e+6 psi | Average value: 503 MPa Grade Count:3 |
| 0.000 - 30.0 MPa @Temperature 100 - 100 °C | 0.000 - 4350 psi @Temperature 212 - 212 °F | Average value: 15.0 MPa Grade Count:1 | |
| 0.000 - 30.0 MPa @Strain 0.000 - 1.56 % | 0.000 - 4350 psi @Strain 0.000 - 1.56 % | Average value: 15.0 MPa Grade Count:1 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 3.30e+17 ohm-cm | 1.00e+13 - 3.30e+17 ohm-cm | Average value: 1.77e+16 ohm-cm Grade Count:33 |
| Surface Resistance | 1.00e+13 - 3.00e+15 ohm | 1.00e+13 - 3.00e+15 ohm | Average value: 4.02e+14 ohm Grade Count:19 |
| Dielectric Constant | 2.83 - 4.80 | 2.83 - 4.80 | Average value: 3.77 Grade Count:25 |
| Dielectric Strength | 18.0 - 40.0 kV/mm | 457 - 1020 kV/in | Average value: 24.9 kV/mm Grade Count:25 |
| 9.00 - 24.0 kV/mm @Temperature 95.0 - 150 °C | 229 - 610 kV/in @Temperature 203 - 302 °F | Average value: 16.5 kV/mm Grade Count:3 | |
| 9.00 - 24.0 kV/mm @Thickness 1.60 - 3.20 mm | 229 - 610 kV/in @Thickness 0.0630 - 0.126 in | Average value: 16.5 kV/mm Grade Count:3 | |
| Dissipation Factor | 0.00100 - 0.0210 | 0.00100 - 0.0210 | Average value: 0.0125 Grade Count:16 |
| Arc Resistance | 77.0 - 129 sec | 77.0 - 129 sec | Average value: 109 sec Grade Count:11 |
| Comparative Tracking Index | 15.0 - 400 V | 15.0 - 400 V | Average value: 243 V Grade Count:19 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 - 500 μm/m-°C | 10.0 - 278 μin/in-°F | Average value: 283 μm/m-°C Grade Count:21 |
| 500 - 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 μin/in-°F @Temperature 131 - 320 °F | Average value: 500 μm/m-°C Grade Count:4 | |
| CTE, linear, Transverse to Flow | 64.0 - 122 μm/m-°C | 35.6 - 67.8 μin/in-°F | Average value: 88.1 μm/m-°C Grade Count:8 |
| 92.0 - 121 μm/m-°C @Temperature 55.0 - 160 °C | 51.1 - 67.2 μin/in-°F @Temperature 131 - 320 °F | Average value: 102 μm/m-°C Grade Count:4 | |
| Melting Point | 232 - 260 °C | 450 - 500 °F | Average value: 251 °C Grade Count:37 |
| Maximum Service Temperature, Air | 75.0 - 150 °C | 167 - 302 °F | Average value: 110 °C Grade Count:4 |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 - 255 °C | 433 - 491 °F | Average value: 242 °C Grade Count:37 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 - 242 °C | 230 - 468 °F | Average value: 219 °C Grade Count:58 |
| Vicat Softening Point | 225 - 260 °C | 437 - 500 °F | Average value: 232 °C Grade Count:8 |
| UL RTI, Electrical | 140 - 155 °C | 284 - 311 °F | Average value: 150 °C Grade Count:8 |
| UL RTI, Mechanical with Impact | 140 - 155 °C | 284 - 311 °F | Average value: 149 °C Grade Count:8 |
| UL RTI, Mechanical without Impact | 140 - 155 °C | 284 - 311 °F | Average value: 149 °C Grade Count:10 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:52 |
| Oxygen Index | 20.0 - 33.0 % | 20.0 - 33.0 % | Average value: 26.4 % Grade Count:6 |
| Glow Wire Test | 750 - 985 °C | 1380 - 1810 °F | Average value: 903 °C Grade Count:14 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 293 °C | 68.0 - 560 °F | Average value: 232 °C Grade Count:17 |
| Feed Temperature | 40.0 - 270 °C | 104 - 518 °F | Average value: 118 °C Grade Count:14 |
| Nozzle Temperature | 260 - 300 °C | 500 - 572 °F | Average value: 281 °C Grade Count:8 |
| Melt Temperature | 235 - 300 °C | 455 - 572 °F | Average value: 275 °C Grade Count:27 |
| Mold Temperature | 73.9 - 163 °C | 165 - 325 °F | Average value: 113 °C Grade Count:43 |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | Average value: 127 °C Grade Count:28 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.89 hour Grade Count:27 |
| Moisture Content | 0.0100 - 0.0800 % | 0.0100 - 0.0800 % | Average value: 0.0413 % Grade Count:23 |
| Dew Point | -40.0 - -30.0 °C | -40.0 - -22.0 °F | Average value: -37.5 °C Grade Count:4 |
| Injection Pressure | 50.0 - 120 MPa | 7250 - 17400 psi | Average value: 78.6 MPa Grade Count:9 |
| Hold Pressure | 30.0 - 100 MPa | 4350 - 14500 psi | Average value: 71.8 MPa Grade Count:13 |
| Back Pressure | 0.000 - 2.00 MPa | 0.000 - 290 psi | Average value: 0.421 MPa Grade Count:6 |
| Screw Speed | 50.0 - 200 rpm | 50.0 - 200 rpm | Average value: 90.4 rpm Grade Count:5 |