- 密度 [g/cm3]: 1.64
- 缺口沖擊強度: 7.3
- 彎曲模量 [MPa]: 4.609
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.090 % | 0.090 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 4.10 GPa | 595 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 68.0 MPa | 9860 psi | ISO 178 |
| Flexural Modulus | 4.609 GPa | 668.5 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.30 kJ/m2 | 3.47 ft-lb/in2 | ISO 180/1A |
| Charpy Impact Unnotched | 2.20 J/cm2 | 10.5 ft-lb/in2 | ISO 179/1eU |
| 5.40 J/cm2 @Temperature 30.0 °C | 25.7 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO 179/1eA |
| 0.310 J/cm2 @Temperature 30.0 °C | 1.48 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 7.00e+12 ohm-cm | 7.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 4.4 @Frequency 1.00e+6 Hz | 4.4 @Frequency 1.00e+6 Hz | IEC 60250 |
| 4.7 @Frequency 100 Hz | 4.7 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.024 @Frequency 1.00e+6 Hz | 0.024 @Frequency 1.00e+6 Hz | IEC 60250 |
| 0.026 @Frequency 100 Hz | 0.026 @Frequency 100 Hz | IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ISO 75-1, -2 |
| Glass Transition Temp, Tg | 73.0 °C | 163 °F | ISO 11357-1,-2,-3 |