- 密度 [g/cm3]: 1.69
- 缺口沖擊強度: 3.1
- 彎曲模量 [MPa]: 12.0
- 熱變形溫度 [℃]: 184.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.69 g/cc | 0.0611 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0025 - 0.0045 cm/cm | 0.0025 - 0.0045 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 79.0 MPa | 11500 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.0 % | 1.0 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 11.9 GPa | 1730 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 131 MPa | 19000 psi | ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.10 kJ/m2 | 1.48 ft-lb/in2 | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 184 °C | 363 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 | V-0 | |