- 熔體流動(dòng)速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.5
- 缺口沖擊強(qiáng)度: 1.33
- 彎曲模量 [MPa]: 9.00
- 熱變形溫度 [℃]: 223.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 | ||
| Density | 1.50 g/cc | 0.0542 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ISO 294-4 | ||
| 0.0050 cm/cm | 0.0050 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ISO 294-4 | ||
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 71 | 71 | ISO 2039-2 | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | 5mm/min; ISO 527-2/1A | ||
| 110 MPa @Temperature 22.8 °C | 16000 psi @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527-2/1A | ||
| 4.0 % @Temperature 22.8 °C | 4.0 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 9.50 GPa | 1380 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 | ||
| 172 MPa @Temperature 22.8 °C | 25000 psi @Temperature 73.0 °F | ASTM D790 | |||
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 | ||
| 8.27 GPa @Temperature 22.8 °C | 1200 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 1.33 J/cm @Temperature 22.8 °C | 2.50 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 13.2 kJ/m2 | 6.28 ft-lb/in2 | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.40 J/cm2 | 25.7 ft-lb/in2 | ISO 179/1eU | ||
| 5.40 J/cm2 @Temperature 30.0 °C | 25.7 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.31 J/cm2 | 6.23 ft-lb/in2 | ISO 179/1eA | ||
| 1.32 J/cm2 @Temperature 30.0 °C | 6.28 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Strength | 21.7 kV/mm | 550 kV/in | short term; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 μm/m-°C | 11.1 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 65.0 μm/m-°C | 36.1 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 | ||
| 224 °C | 435 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75-1, -2 | ||
| 209 °C | 408 °F | ASTM D648 | |||
| Flammability, UL94 | HB | HB | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 260 °C | 500 °F | ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Injection Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Melt volume rate (MVR), cm3/10min | 5.7 | ||||
| MVR test load, kg | 2.16 | ||||
| MVR test temperature, °C | 250 | ||||
| Processing conditions acc. ISO | 7792-2 | ||||