- 密度 [g/cm3]: 1.49
- 缺口沖擊強度: 1.17
- 彎曲模量 [MPa]: 8.70
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 | ||
| Density | 1.49 g/cc | 0.0538 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ISO 294-4 | ||
| 0.0030 cm/cm | 0.0030 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2/1A | ||
| 110 MPa @Temperature 22.8 °C | 16000 psi @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Break | 2.8 % | 2.8 % | 5mm/min; ISO 527-2/1A | ||
| 3.0 % @Temperature 22.8 °C | 3.0 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 8.50 GPa | 1230 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 | ||
| 172 MPa @Temperature 22.8 °C | 25000 psi @Temperature 73.0 °F | ASTM D790 | |||
| Flexural Modulus | 8.70 GPa | 1260 ksi | ISO 178 | ||
| 7.58 GPa @Temperature 22.8 °C | 1100 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 1.17 J/cm @Temperature 22.8 °C | 2.20 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 13.9 kJ/m2 | 6.61 ft-lb/in2 | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.60 J/cm2 | 26.6 ft-lb/in2 | ISO 179/1eU | ||
| 4.10 J/cm2 @Temperature 30.0 °C | 19.5 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.990 J/cm2 | 4.71 ft-lb/in2 | ISO 179/1eA | ||
| 0.830 J/cm2 @Temperature 30.0 °C | 3.95 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 | ||
| Dielectric Constant | 2.5 @Frequency 1.00e+6 Hz | 2.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.2 @Frequency 100 Hz | 3.2 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | IEC 60243-1 | ||
| 21.1 kV/mm | 536 kV/in | short term; ASTM D149 | |||
| Dissipation Factor | 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 300 V | 300 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 23.0 μm/m-°C | 12.8 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 24.0 μm/m-°C | 13.3 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | ASTM D648 | ||
| 218 °C | 424 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 173 °C | 343 °F | ISO 75-1, -2 | ||
| 173 °C | 344 °F | ASTM D648 | |||
| Glass Transition Temp, Tg | 55.0 °C | 131 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | HB | HB | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 260 °C | 500 °F | ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Injection Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Processing conditions acc. ISO | 7792-2 | ||||