- 密度 [g/cm3]: 1.61
- 缺口沖擊強度: 10.0
- 彎曲模量 [MPa]: 12.1
- 熱變形溫度 [℃]: 226.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.4 % | 2.4 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 12.5 GPa | 1810 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 | ||
| Flexural Modulus | 12.1 GPa | 1750 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 | 4.76 ft-lb/in2 | ISO 180/1A | ||
| Charpy Impact, Notched | 1.00 J/cm2 | 4.76 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | IEC 60243-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 μm/m-°C | 8.33 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | ISO 75-1, -2 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | |||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||