- 密度 [g/cm3]: 1.29
- 缺口沖擊強(qiáng)度: 0.694
- 彎曲模量 [MPa]: 4.23
- 熱變形溫度 [℃]: 202.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 | ||
| Density | 1.29 g/cc | 0.0466 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ISO 294-4 | ||
| 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 83.0 MPa | 12000 psi | 5mm/min; ISO 527-2/1A | ||
| 65.5 MPa @Temperature 22.8 °C | 9500 psi @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527-2/1A | ||
| 5.0 % @Temperature 22.8 °C | 5.0 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 4.48 GPa @Temperature 22.8 °C | 650 ksi @Temperature 73.0 °F | ASTM D638 | ||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 | ||
| 111 MPa @Temperature 22.8 °C | 16100 psi @Temperature 73.0 °F | ASTM D790 | |||
| Flexural Modulus | 4.23 GPa | 614 ksi | ISO 178 | ||
| 3.59 GPa @Temperature 22.8 °C | 520 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.694 J/cm @Temperature 22.8 °C | 1.30 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1U | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.20e+17 ohm-cm | 1.20e+17 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz | 3.4 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| Dielectric Strength | 16.5 kV/mm | 420 kV/in | short term; ASTM D149 | ||
| Dissipation Factor | 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| Arc Resistance | 129 sec | 129 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 107 °C | 225 °F | ASTM D3418 | ||
| 225 °C | 437 °F | ISO 11357-1,-2,-3 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | HB | HB | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection speed | medium-fast | ||||