| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Break | 2.0 % | 2.0 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact, Notched | 0.560 J/cm2 | 2.66 ft-lb/in2 | ISO 179/1eA |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper |
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |
| Feed Temperature | 230 - 250 °C | 446 - 482 °F | |
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |
| Zone 2 | 235 - 255 °C | 455 - 491 °F | |
| Zone 3 | 235 - 255 °C | 455 - 491 °F | |
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |
| Die Temperature | 250 - 265 °C | 482 - 509 °F | |
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | |
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |