- 密度 [g/cm3]: 1.74
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.587
- 彎曲模量 [MPa]: 9.45
- 熱變形溫度 [℃]: 212.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.74 g/cc | 1.74 g/cc | ASTM D792 | ||
| Density | 1.74 g/cc | 0.0629 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.10 % @Temperature 22.8 °C | 0.10 % @Temperature 73.0 °F | 24hr immersion; ASTM D570 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 43 | 43 | ISO 2039-2 | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5mm/min; ISO 527-2/1A | ||
| 75.8 MPa @Temperature 22.8 °C | 11000 psi @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Break | 1.8 % | 1.8 % | 5mm/min; ISO 527-2/1A | ||
| 1.9 % @Temperature 22.8 °C | 1.9 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 | ||
| 121 MPa @Temperature 22.8 °C | 17500 psi @Temperature 73.0 °F | ASTM D790 | |||
| Flexural Modulus | 9.45 GPa | 1370 ksi | ISO 178 | ||
| 9.65 GPa @Temperature 22.8 °C | 1400 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.587 J/cm @Temperature 22.8 °C | 1.10 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | ISO 180/1A | ||
| Charpy Impact Unnotched | 2.90 J/cm2 | 13.8 ft-lb/in2 | ISO 179/1eU | ||
| 2.90 J/cm2 @Temperature 30.0 °C | 13.8 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.670 J/cm2 | 3.19 ft-lb/in2 | ISO 179/1eA | ||
| 0.670 J/cm2 @Temperature 30.0 °C | 3.19 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| Dielectric Strength | 18.5 kV/mm | 470 kV/in | short term; ASTM D149 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| Arc Resistance | 123 sec | 123 sec | ASTM D495 | ||
| Comparative Tracking Index | 300 V | 300 V | ASTM D3638 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 30.0 μm/m-°C | 16.7 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 55.0 μm/m-°C | 30.6 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ISO 75-1, -2 | ||
| 214 °C | 417 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 184 °C | 363 °F | ISO 75-1, -2 | ||
| 195 °C | 383 °F | ASTM D648 | |||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| V-0 @Thickness 0.850 mm | V-0 @Thickness 0.0335 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 96.0 °C | 149 - 205 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 255 °C | 464 - 491 °F | |||
| Die Temperature | 240 - 255 °C | 464 - 491 °F | |||
| Melt Temperature | 235 - 255 °C | 455 - 491 °F | |||
| 260 °C | 500 °F | ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Injection Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Processing conditions acc. ISO | 7792 | ||||