- 密度 [g/cm3]: 1.57
- 缺口沖擊強度: 0.854
- 彎曲模量 [MPa]: 9.20
- 熱變形溫度 [℃]: 225.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0030 cm/cm | 0.0015 - 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 105 MPa | 15200 psi | 5mm/min; ISO 527-2/1A |
| 107 MPa @Temperature 22.8 °C | 15500 psi @Temperature 73.0 °F | ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | 5mm/min; ISO 527-2/1A |
| 3.0 % @Temperature 22.8 °C | 3.0 % @Temperature 73.0 °F | ASTM D638 | |
| Tensile Modulus | 9.10 GPa | 1320 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 165 MPa | 23900 psi | ISO 178 |
| 172 MPa @Temperature 22.8 °C | 25000 psi @Temperature 73.0 °F | ASTM D790 | |
| Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178 |
| 8.62 GPa @Temperature 22.8 °C | 1250 ksi @Temperature 73.0 °F | ASTM D790 | |
| Izod Impact, Notched | 0.854 J/cm @Temperature 22.8 °C | 1.60 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m2 | 3.81 ft-lb/in2 | ISO 180/1A |
| Charpy Impact, Notched | 0.790 J/cm2 | 3.76 ft-lb/in2 | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |