- 密度 [g/cm3]: 1.46
- 缺口沖擊強度: 3.5
- 彎曲模量 [MPa]: 3.30
- 熱變形溫度 [℃]: 168.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.19 % | 0.19 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 8.5 % | 8.5 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 3.30 GPa | 479 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 3.30 GPa | 479 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m2 | 1.67 ft-lb/in2 | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.3 kJ/m2 @Temperature 23.0 °C | 7.28 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1U |
| Charpy Impact Unnotched | 2.20 J/cm2 | 10.5 ft-lb/in2 | ISO 179/1eU |
| 1.90 J/cm2 @Temperature 30.0 °C | 9.04 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.170 J/cm2 | 0.809 ft-lb/in2 | ISO 179/1eA |
| 0.280 J/cm2 @Temperature 30.0 °C | 1.33 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.00e+14 ohm-cm | 3.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz | 3.5 @Frequency 1.00e+6 Hz | IEC 60250 |
| 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | IEC 60250 |
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 77.0 μm/m-°C | 42.8 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 77.0 μm/m-°C | 42.8 μin/in-°F | ISO 11359-2 |
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75-1, -2 |
| Glass Transition Temp, Tg | 50.0 °C | 122 °F | ISO 11357-1,-2,-3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper |
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |