- 熔體流動速率 [g/10min]: 22.0
- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 5.5
- 彎曲強度 [MPa]: 93.0
- 彎曲模量 [MPa]: 5.20
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.20 % | 0.20 % | 24 hour; ISO Test | ||
| 0.40 % | 0.40 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 113 cm3/g | 113 cm3/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 250 °C | 22 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 93.0 MPa | 13500 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.8 % | 3.8 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 5.70 GPa | 827 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 5.50 kJ/m2 | 2.62 ft-lb/in2 | ISO Test | ||
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| 223 °C | 433 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||||
| Descriptive Properties | |||||
| Color | BK5110 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| NSF Std. 61 | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| U.V. stabilized or stable to weather | |||||