- 熔體流動速率 [g/10min]: 30.0
- 密度 [g/cm3]: 1.68
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | similar to ISO 62 test | ||
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 260 °C | 30 g/10 min @Load 11.0 lb, Temperature 500 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-1 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1 | ||
| Tensile Modulus | 16.5 GPa | 2390 ksi | ISO 527-1 | ||
| Charpy Impact Unnotched | 6.50 J/cm2 | 30.9 ft-lb/in2 | ISO 179-1eU | ||
| Charpy Impact, Notched | 1.10 J/cm2 | 5.23 ft-lb/in2 | ISO 179-1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL Registered; IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Resin Type | (PBT+X)-GF45 | ||||